Product display Product

Product display

PVB Film (High-end)

Product introduction

Product description

A new material designed for photovoltaic applications

In developed countries, the advantages of integrated photovoltaic systems for buildings are increasing. In the context of increasing global energy costs, in order to assess the potential of photovoltaic building integration, architects and engineers are studying the use of photovoltaics for glass curtain walls and roofs and cost-effective integrated solutions, because photovoltaic modules themselves are a A special kind of laminated glass (encapsulated solar crystalline silicon wafer), then by producing photovoltaic modules with new safety and protection characteristics, it will have its own advantages. This new development makes photovoltaic building integration more attractive to architects and adds new opportunities to the future of photovoltaic module manufacturers, the construction industry, and the glass industry.

Huakai, as one of the largest PVB interlayer suppliers in China in the construction and automotive industry, developed it for its deep understanding of the growing importance of the photovoltaic market in the field of renewable energy. Used in special photovoltaic PVB interlayer. The solar cell module of the PVB interlayer for photovoltaic modules produced by Huakai shows high transparency, high adsorption power and excellent thermal insulation, ultraviolet protection, and moisture resistance. They are still highly reliable when exposed to harsh outdoor weather conditions for long periods of time.

After Huakai PVB interlayer film is laminated and cross-linked and cured, it can not only increase the bonding degree of the battery module, enhance the efficiency of the solar cell module, but also provide mechanical, thermal and optical protection for the module, extend the service life of the module, and increase the cost. benefit.

Technical parameters of photovoltaic grade PVB

Feature

unit

Tech-standards

Detection method

Density  

g/cm3

1.070

GB/T1033-1986

Tensile strength

Mpa

≥22

GB/T1040-1992

Elongation at break

%

>200

GB/T1040-1992

Moisture content

%

0.35-0.55

企标

Transmittance

%

≥89

GB/T2410-1998

Haze

%

≤0.4

GB/T2410-1998

Thermal expansion

℃-1

2.2×10-4

GB/T1036-1989

Volume resistivity

ΩCm×1011

8.0

GB/T1014-2006

Adhesive strength

N/cm

≥20

GB/T1751-1998

Yellowing index

N/A--

≤12

HG/T3862-2006

UV shielding

300-400nm

≤4.0

-- 

Photovoltaic grade transparent sheet  (0.50/0.76mm)   

 

Thickness

0.50/0.76mm

colour

Transparent film

Porcelain white

Width

650-2440

Length                                      

300/200